电磁超声换能器一般采用具有超强磁力的稀土永磁制作,在实际检测中由于磁力不可控,存在偏置磁场不够强导致换能效率过低和磁力过强造成操作不方便等问题.提出一种偏置磁场磁力可控的电磁超声换能器,采用电磁铁与永磁铁相结合的方式,达到偏置磁场磁力可控的目的.通过有限元仿真和试验得出,提出的偏置磁场磁力可控的电磁超声换能器,在电磁铁处于关闭模式下,永磁铁能够提供基础磁场;采用增强模式或减弱模式,无被测物时,换能器下表面平均垂直磁通最大分别增强78.58％和减弱19.36％,而提离2 mm检测钢板时,换能器下方钢板表面平均垂直磁通最大分别增强52.99％和减弱38.02％;得出3种模式下,探头磁力随着提离距离缩小而增强的试验曲线;通过增强模式对铝板和钢板进行测厚试验,将检测信号幅值分别提高46.91％和62.01％.所设计的磁力可控电磁超声换能器不仅具有磁力可控的功能,还能够提高检测信号幅值.     

4,6-二氯嘧啶合成工艺研究

4,6-二氯嘧啶是一种重要的化工中间体.研究了反应温度、溶剂种类、催化剂种类、催化剂用量和反应物投料配比在4,6-二氯嘧啶合成过程中对反应的影响.结果 表明,在以邻硝基甲苯为溶剂,苄基三乙基氯化铵为催化剂,且催化剂用量为4,6-二羟基嘧啶质量的2％,n(4,6-二羟基嘧啶):n(三光气)=1∶0.8,反应温度为100～110℃的最佳条件下,产品收率可以达到93.4％.     

Mechanical properties and thermal shock in thin ZrO2–Y2O3–Al2O3 films obtained by the sol-gel method

Thin multilayer coatings of ZrO₂–Y₂O₃–Al₂O₃ were prepared using the sol-gel method and dip-coating technique in order to advance in the study of what influence the incorporation of Al₂O₃ has on films of Y₂O₃-doped ZrO₂, investigating its role in the synthesis of the solutions and in the characteristics and properties of the coatings. After the characterization of the solutions used in the process, the microstructure of the films was studied and their mechanical behaviour and resistance to thermal shock were determined so as to optimize the characteristics and functionality of these coatings. With increased alumina content, 3YSZ-Al₂O₃ (20 mol%), the cubic phase of the zirconia disappeared completely at the sintering temperature used (700 °C), resulting in the tetragonal phase with Al in solution. There was also a decrease in the coatings' hardness and Young's modulus, and an increase in toughness and resistance to thermal shock. These results allow guidelines to be established for the design of multilayer structures that are, tougher, more resistant, and have improved surface properties.     

Characterization of precipitates formed in X7R 0603 BME-MLCC during sintering

In the current study two different batches of X7R-0603 BME-MLCCs displayed dissimilar electrical performance, despite having the same chemical composition, tape casting, and sintering conditions; with the only difference between them being the ore deposits where the raw materials were extracted from to synthesize the BaTiO₃. Specifically, they presented different electrical response to highly accelerated life tests (HALT). Although the chemical analysis of each slip showed the same composition, the trace elements of the BaTiO₃ sources could have acted as dopants or produced different secondary phases. A search for precipitates in the two samples was conducted by means of Scanning (SEM) and Transmission Electron Microscopy (TEM) techniques. SEM observations confirmed the presence of precipitates formed within the structure of the MLCCs exhibiting the greatest decrement in their electrical resistance results during the HALT. In order to further characterize the observed precipitates, samples were prepared by Focused Ion Beam (FIB) lift-out method, to make TEM characterization of specific precipitates feasible. TEM studies were performed on the precipitates to obtain electron diffraction patterns and complementary Energy Dispersive X-Ray Spectroscopy (EDXS) chemical analysis. Based on the crystal and chemical data obtained, it can be concluded that the precipitates are a hexagonal anhydrous silicate oxyapatite phase with a stoichiometry of Ca₃Y₁₆Si₁₀O₁₃, and lattice parameters of a = 0.9353 nm and c = 0.6970 nm; this phase was not found in the JCPDS data base. Differences in raw materials coming from different ore deposits can produce undesired precipitates that affect the electrical performance of MLCCs.     

Centrifugally spun carbon fibers prepared from aqueous poly(vinylpyrrolidone) solutions as binder-free anodes in lithium-ion batteries

Aqueous solutions of poly(vinylpyrrolidone) (PVP) of various concentrations (20, 25, and 28 wt%) were successfully spun into fibers by centrifugal spinning. The pristine PVP fibers were annealed and carbonized to produce flexible carbon fibers for use as binder-free anodes in lithium-ion batteries. These flexible carbon fibers were prepared by developing a novel three-step heat treatment to reduce the residual stresses in the pristine PVP precursor fibers, and to prevent fiber degradation during carbonization. The thermogravimetric analysis data showed that the annealed fibers yielded a residual mass percentage of 36.0% while the pristine PVP fibers suffered a higher mass loss and only retained 26.5% of original mass above 450 °C (under nitrogen). The electrochemical performance of the carbon-fiber anodes was evaluated by conducting galvanostatic charge/discharge, rate performance, and cycle voltammetry experiments. The 20, 25, and 28 wt% derived binder-free anodes delivered specific charge capacities of 205, 189, and 275 mAh g⁻¹, respectively, after the first cycle at a current density of 100 mA g⁻¹. The results obtained in this work indicate that a feasible pathway towards a large-scale production of carbon-fiber anodes from a 100% aqueous solution can be achieved via centrifugal spinning and subsequent heat treatment.     

基于电沉积法回收废水中铝离子的最佳工艺参数分析

基于电沉积法,针对某铝箔生产企业所产生的高含铝离子废水,通过不同峰值电流密度下形成的电沉积试样的相关电化学曲线测试结果和镀层中的Al质量分数分析,确定所采用电沉积法的最佳峰值电流密度为9 A·dm-2,此时沉积层中铝质量分数为33.21％,原子数量占比为24.69％.     

具有良好时频性能的电力系统次同步振荡模态在线辨识算法

介绍了一种适用于电力系统次同步振荡在线监测的非平稳信号模态辨识算法,该算法综合了经典IIR窄带滤波器组算法及经验模态分解(empirical mode decomposition,EMD)算法的优点,利用次同步振荡分析获得的预知频率信息,对可能导致模态混叠的相邻模态做数字滤波器(Infinite Impulse Response,IIR)预处理,再经EMD获得无混叠的固有模态分量IMF1.该算法具有理想的窄带选频特性,且能够快速反映次同步振荡及机组扭振发生最初的时域过程,计算量很小,可用于现场在线提取SSO模态特征,有利于更好地实现对次同步振荡的稳定性判别及闭环控制、机组扭振保护等.最后,利用PSCAD产生的仿真数据及某电厂发生次同步振荡的现场数据验证了该算法的有效性.     

CrN和CrN/Ag涂层的真空高温摩擦磨损性能*

为改善涂层在真空、高温等苛刻条件下的摩擦学性能，利用中频直流磁控溅射技术在硅片和316L不锈钢上沉积了CrN和CrN/Ag涂层，利用扫描电镜、透射电镜和X射线衍射仪对涂层的成分及相结构进行了表征，通过划痕测试仪、纳米压痕仪和摩擦磨损试验机测试了涂层的力学及摩擦学性能。结果表明：添加Ag元素以后，CrN/Ag涂层硬度及承载能力有所减小，但结合强度增加；真空高温环境下CrN与CrN/Ag涂层摩擦因数随温度升高呈下降趋势，其中CrN涂层通过软化镀层减小剪切强度和阻力，从而减小摩擦因数，CrN/Ag涂层主要通过高温产生的热驱动力诱导表面Ag润滑膜的形成来减小摩擦因数；CrN涂层依靠自身剪切特性参与摩擦，而CrN/Ag涂层在真空高温下具有自润滑和持续润滑性能，作为自润滑零部件具有潜在的应用价值。